#$Date: 2021-04-27 12:29:29 +0300 (Tue, 27 Apr 2021) $
#$Revision: 264589 $
#$URL: file:///home/coder/svn-repositories/cod/cif/1/56/21/1562164.cif $
#------------------------------------------------------------------------------
#
# This file is available in the Crystallography Open Database (COD),
# http://www.crystallography.net/
#
# All data on this site have been placed in the public domain by the
# contributors.
#
data_1562164
loop_
_publ_author_name
'Jin, Geng Bang'
'Soderholm, L.'
_publ_section_title
;
 Solid-state syntheses and single-crystal characterizations of three
 tetravalent thorium and uranium silicates
;
_journal_name_full               'Journal of Solid State Chemistry'
_journal_page_first              405
_journal_page_last               410
_journal_paper_doi               10.1016/j.jssc.2014.10.018
_journal_volume                  221
_journal_year                    2015
_chemical_formula_moiety         '(Ca0.5 Na0.5)2 Na U Si8 O20'
_chemical_formula_sum            'Ca Na2 O20 Si8 U'
_chemical_formula_weight         868.81
_chemical_name_common            'Calcium sodium uranium silicate'
_space_group_IT_number           124
_space_group_name_Hall           '-P 4 2c'
_space_group_name_H-M_alt        'P 4/m c c'
_symmetry_cell_setting           tetragonal
_symmetry_space_group_name_H-M   'P 4/m c c'
_atom_sites_solution_primary     direct
_atom_sites_solution_secondary   difmap
_audit_creation_method           SHELXL-97
_cell_angle_alpha                90.00
_cell_angle_beta                 90.00
_cell_angle_gamma                90.00
_cell_formula_units_Z            2
_cell_length_a                   7.4379(16)
_cell_length_b                   7.4379(16)
_cell_length_c                   14.888(3)
_cell_measurement_reflns_used    2313
_cell_measurement_temperature    100(2)
_cell_measurement_theta_max      29.74
_cell_measurement_theta_min      4.75
_cell_volume                     823.6(3)
_computing_cell_refinement       'Bruker APEX2'
_computing_data_collection       'Bruker APEX2'
_computing_data_reduction        'Bruker SAINT'
_computing_molecular_graphics    'CrystalMaker for Windows ver. 2.5.2 (2011)'
_computing_publication_material  'SHELXTL-97 (Sheldrick, 1997)'
_computing_structure_refinement  'SHELXL-97 (Sheldrick, 1997)'
_computing_structure_solution    'SHELXS-97 (Sheldrick, 1990)'
_diffrn_ambient_temperature      100(2)
_diffrn_measured_fraction_theta_full 0.994
_diffrn_measured_fraction_theta_max 0.994
_diffrn_measurement_device_type  'Bruker APEX-II CCD'
_diffrn_measurement_method       '0.3 wide w/ exposures'
_diffrn_radiation_monochromator  graphite
_diffrn_radiation_source         'fine-focus sealed tube'
_diffrn_radiation_type           MoK\a
_diffrn_radiation_wavelength     0.71073
_diffrn_reflns_av_R_equivalents  0.0635
_diffrn_reflns_av_sigmaI/netI    0.0225
_diffrn_reflns_limit_h_max       10
_diffrn_reflns_limit_h_min       -10
_diffrn_reflns_limit_k_max       10
_diffrn_reflns_limit_k_min       -10
_diffrn_reflns_limit_l_max       21
_diffrn_reflns_limit_l_min       -21
_diffrn_reflns_number            11179
_diffrn_reflns_theta_full        31.10
_diffrn_reflns_theta_max         31.10
_diffrn_reflns_theta_min         4.75
_diffrn_standards_number         0
_exptl_absorpt_coefficient_mu    10.915
_exptl_absorpt_correction_T_max  0.804
_exptl_absorpt_correction_T_min  0.583
_exptl_absorpt_correction_type   multi-scan
_exptl_absorpt_process_details   SADABS
_exptl_crystal_colour            green
_exptl_crystal_density_diffrn    3.503
_exptl_crystal_density_method    'not measured'
_exptl_crystal_description       'irregular prism'
_exptl_crystal_F_000             812
_exptl_crystal_size_max          0.065
_exptl_crystal_size_mid          0.042
_exptl_crystal_size_min          0.020
_refine_diff_density_max         1.800
_refine_diff_density_min         -1.040
_refine_diff_density_rms         0.237
_refine_ls_extinction_method     none
_refine_ls_goodness_of_fit_ref   1.267
_refine_ls_matrix_type           full
_refine_ls_number_parameters     41
_refine_ls_number_reflns         692
_refine_ls_number_restraints     0
_refine_ls_restrained_S_all      1.267
_refine_ls_R_factor_all          0.0388
_refine_ls_R_factor_gt           0.0292
_refine_ls_shift/su_max          0.000
_refine_ls_shift/su_mean         0.000
_refine_ls_structure_factor_coef Fsqd
_refine_ls_weighting_details
; calc 
 [1.00000+0.00000exp(0.00(sinθ/λ)²)]/ 
   [σ²(Fo²)+0.0000+0.0000*P+(0.0450P)²+0.0000sinθ/λ] 
 where P = 1.00000Fo² + 0.00000Fc² 
;
_refine_ls_weighting_scheme      calc
_refine_ls_wR_factor_gt          0.0727
_refine_ls_wR_factor_ref         0.0793
_reflns_number_gt                567
_reflns_number_total             692
_reflns_threshold_expression     >2sigma(I)
_cod_data_source_file            JSSC-2015-221-405.cif
_cod_data_source_block           compound3
_cod_depositor_comments
;
The following automatic conversions were performed:

data item '_exptl_crystal_density_meas' value 'not measured' was
changed to '?' -- the value is perceived as not measured.

Automatic conversion script
Id: cif_fix_values 8369 2020-08-20 11:38:08Z andrius 
;
_cod_original_cell_volume        823.7(3)
_cod_database_code               1562164
loop_
_symmetry_equiv_pos_as_xyz
'x, y, z'
'-x, -y, z'
'-y, x, z'
'y, -x, z'
'-x, y, -z+1/2'
'x, -y, -z+1/2'
'y, x, -z+1/2'
'-y, -x, -z+1/2'
'-x, -y, -z'
'x, y, -z'
'y, -x, -z'
'-y, x, -z'
'x, -y, z-1/2'
'-x, y, z-1/2'
'-y, -x, z-1/2'
'y, x, z-1/2'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_adp_type
_atom_site_occupancy
_atom_site_symmetry_multiplicity
_atom_site_calc_flag
_atom_site_refinement_flags
_atom_site_disorder_assembly
_atom_site_disorder_group
Ca1 Ca 0.0000 0.5000 0.2500 0.0092(4) Uani 0.50 4 d SP . .
Na1 Na 0.0000 0.5000 0.2500 0.0092(4) Uani 0.50 4 d SP . .
Na2 Na 0.0000 0.0000 0.0000 0.0392(19) Uani 1 8 d S . .
U1 U 0.0000 0.0000 0.2500 0.00873(15) Uani 1 8 d S . .
Si1 Si 0.25672(17) 0.32905(18) 0.10533(9) 0.0122(3) Uani 1 1 d . . .
O1 O 0.1033(5) 0.2459(5) 0.1652(2) 0.0199(7) Uani 1 1 d . . .
O2 O 0.4553(5) 0.2535(5) 0.1272(3) 0.0209(8) Uani 1 1 d . . .
O3 O 0.2161(9) 0.2933(9) 0.0000 0.0293(13) Uani 1 2 d S . .
loop_
_atom_type_symbol
_atom_type_description
_atom_type_scat_dispersion_real
_atom_type_scat_dispersion_imag
_atom_type_scat_source
O O 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Na Na 0.0362 0.0249 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Si Si 0.0817 0.0704 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Ca Ca 0.2262 0.3064 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
U U -9.6767 9.6646 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
O1 Ca1 O1 142.64(18) . 6_565
O1 Ca1 O1 76.04(17) . 5
O1 Ca1 O1 116.51(17) 6_565 5
O1 Ca1 O1 116.51(17) . 2_565
O1 Ca1 O1 76.04(17) 6_565 2_565
O1 Ca1 O1 142.64(18) 5 2_565
O1 Ca1 O2 76.47(12) . 3
O1 Ca1 O2 133.65(12) 6_565 3
O1 Ca1 O2 92.08(13) 5 3
O1 Ca1 O2 60.49(12) 2_565 3
O1 Ca1 O2 92.08(13) . 7
O1 Ca1 O2 60.49(12) 6_565 7
O1 Ca1 O2 76.47(12) 5 7
O1 Ca1 O2 133.65(12) 2_565 7
O2 Ca1 O2 165.58(16) 3 7
O1 Ca1 O2 133.65(12) . 8_565
O1 Ca1 O2 76.47(12) 6_565 8_565
O1 Ca1 O2 60.49(12) 5 8_565
O1 Ca1 O2 92.08(13) 2_565 8_565
O2 Ca1 O2 89.14(17) 3 8_565
O2 Ca1 O2 92.66(17) 7 8_565
O1 Ca1 O2 60.49(12) . 4_565
O1 Ca1 O2 92.08(13) 6_565 4_565
O1 Ca1 O2 133.65(12) 5 4_565
O1 Ca1 O2 76.47(12) 2_565 4_565
O2 Ca1 O2 92.66(17) 3 4_565
O2 Ca1 O2 89.14(17) 7 4_565
O2 Ca1 O2 165.58(16) 8_565 4_565
O1 Ca1 Si1 118.95(9) . 6_565
O1 Ca1 Si1 29.21(9) 6_565 6_565
O1 Ca1 Si1 98.77(9) 5 6_565
O1 Ca1 Si1 103.66(9) 2_565 6_565
O2 Ca1 Si1 162.86(9) 3 6_565
O2 Ca1 Si1 31.33(8) 7 6_565
O2 Ca1 Si1 84.78(9) 8_565 6_565
O2 Ca1 Si1 89.41(9) 4_565 6_565
O1 Ca1 Si1 98.77(9) . 2_565
O1 Ca1 Si1 103.66(9) 6_565 2_565
O1 Ca1 Si1 118.95(9) 5 2_565
O1 Ca1 Si1 29.21(9) 2_565 2_565
O2 Ca1 Si1 31.33(8) 3 2_565
O2 Ca1 Si1 162.86(9) 7 2_565
O2 Ca1 Si1 89.41(9) 8_565 2_565
O2 Ca1 Si1 84.78(9) 4_565 2_565
Si1 Ca1 Si1 132.33(5) 6_565 2_565
O1 Ca1 Si1 103.66(9) . 5
O1 Ca1 Si1 98.77(9) 6_565 5
O1 Ca1 Si1 29.21(9) 5 5
O1 Ca1 Si1 118.95(9) 2_565 5
O2 Ca1 Si1 89.41(9) 3 5
O2 Ca1 Si1 84.78(9) 7 5
O2 Ca1 Si1 31.33(8) 8_565 5
O2 Ca1 Si1 162.86(9) 4_565 5
Si1 Ca1 Si1 93.61(5) 6_565 5
Si1 Ca1 Si1 105.28(5) 2_565 5
O1 Ca1 Si1 29.21(9) . .
O1 Ca1 Si1 118.95(9) 6_565 .
O1 Ca1 Si1 103.66(9) 5 .
O1 Ca1 Si1 98.77(9) 2_565 .
O2 Ca1 Si1 84.78(9) 3 .
O2 Ca1 Si1 89.41(9) 7 .
O2 Ca1 Si1 162.86(9) 8_565 .
O2 Ca1 Si1 31.33(8) 4_565 .
Si1 Ca1 Si1 105.28(5) 6_565 .
Si1 Ca1 Si1 93.61(5) 2_565 .
Si1 Ca1 Si1 132.33(5) 5 .
O3 Na2 O3 180.00(17) . 9
O3 Na2 O3 90.0 . 11
O3 Na2 O3 90.0 9 11
O3 Na2 O3 90.0 . 3
O3 Na2 O3 90.0 9 3
O3 Na2 O3 180.0(3) 11 3
O3 Na2 O1 127.60(7) . 9
O3 Na2 O1 52.40(7) 9 9
O3 Na2 O1 81.51(11) 11 9
O3 Na2 O1 98.49(11) 3 9
O3 Na2 O1 98.49(11) . 12
O3 Na2 O1 81.51(11) 9 12
O3 Na2 O1 127.60(7) 11 12
O3 Na2 O1 52.40(7) 3 12
O1 Na2 O1 52.71(8) 9 12
O3 Na2 O1 81.51(11) . 4
O3 Na2 O1 98.49(11) 9 4
O3 Na2 O1 52.40(7) 11 4
O3 Na2 O1 127.60(7) 3 4
O1 Na2 O1 127.29(8) 9 4
O1 Na2 O1 180.00(16) 12 4
O3 Na2 O1 81.51(11) . 11
O3 Na2 O1 98.49(11) 9 11
O3 Na2 O1 52.40(7) 11 11
O3 Na2 O1 127.60(7) 3 11
O1 Na2 O1 52.71(8) 9 11
O1 Na2 O1 77.77(13) 12 11
O1 Na2 O1 102.23(13) 4 11
O3 Na2 O1 98.49(11) . 3
O3 Na2 O1 81.51(11) 9 3
O3 Na2 O1 127.60(7) 11 3
O3 Na2 O1 52.40(7) 3 3
O1 Na2 O1 127.29(8) 9 3
O1 Na2 O1 102.23(13) 12 3
O1 Na2 O1 77.77(13) 4 3
O1 Na2 O1 180.00(19) 11 3
O3 Na2 O1 52.40(7) . 10
O3 Na2 O1 127.60(7) 9 10
O3 Na2 O1 98.49(11) 11 10
O3 Na2 O1 81.51(11) 3 10
O1 Na2 O1 77.77(13) 9 10
O1 Na2 O1 52.71(8) 12 10
O1 Na2 O1 127.29(8) 4 10
O1 Na2 O1 52.71(8) 11 10
O1 Na2 O1 127.29(8) 3 10
O3 Na2 O1 127.60(7) . 2
O3 Na2 O1 52.40(7) 9 2
O3 Na2 O1 81.51(11) 11 2
O3 Na2 O1 98.49(11) 3 2
O1 Na2 O1 102.23(13) 9 2
O1 Na2 O1 127.29(8) 12 2
O1 Na2 O1 52.71(8) 4 2
O1 Na2 O1 127.29(8) 11 2
O1 Na2 O1 52.71(8) 3 2
O1 Na2 O1 180.00(15) 10 2
O3 Na2 O1 52.40(7) . .
O3 Na2 O1 127.60(7) 9 .
O3 Na2 O1 98.49(11) 11 .
O3 Na2 O1 81.51(11) 3 .
O1 Na2 O1 180.00(8) 9 .
O1 Na2 O1 127.29(8) 12 .
O1 Na2 O1 52.71(8) 4 .
O1 Na2 O1 127.29(8) 11 .
O1 Na2 O1 52.71(8) 3 .
O1 Na2 O1 102.23(13) 10 .
O1 Na2 O1 77.77(13) 2 .
O3 Na2 Si1 153.15(2) . 9
O3 Na2 Si1 26.85(2) 9 9
O3 Na2 Si1 91.41(13) 11 9
O3 Na2 Si1 88.59(13) 3 9
O1 Na2 Si1 26.90(7) 9 9
O1 Na2 Si1 60.15(7) 12 9
O1 Na2 Si1 119.85(7) 4 9
O1 Na2 Si1 78.21(7) 11 9
O1 Na2 Si1 101.79(7) 3 9
O1 Na2 Si1 100.94(7) 10 9
O1 Na2 Si1 79.06(7) 2 9
O1 Na2 Si1 153.10(7) . 9
O3 Na2 Si1 26.85(2) . 10
O3 Na2 Si1 153.15(2) 9 10
O3 Na2 Si1 88.59(13) 11 10
O3 Na2 Si1 91.41(13) 3 10
O1 Na2 Si1 100.94(7) 9 10
O1 Na2 Si1 78.21(7) 12 10
O1 Na2 Si1 101.79(7) 4 10
O1 Na2 Si1 60.15(7) 11 10
O1 Na2 Si1 119.85(7) 3 10
O1 Na2 Si1 26.90(7) 10 10
O1 Na2 Si1 153.10(7) 2 10
O1 Na2 Si1 79.06(7) . 10
Si1 Na2 Si1 126.40(4) 9 10
O3 Na2 Si1 153.15(2) . 2
O3 Na2 Si1 26.85(2) 9 2
O3 Na2 Si1 91.41(13) 11 2
O3 Na2 Si1 88.59(13) 3 2
O1 Na2 Si1 79.06(7) 9 2
O1 Na2 Si1 101.79(7) 12 2
O1 Na2 Si1 78.21(7) 4 2
O1 Na2 Si1 119.85(7) 11 2
O1 Na2 Si1 60.15(7) 3 2
O1 Na2 Si1 153.10(7) 10 2
O1 Na2 Si1 26.90(7) 2 2
O1 Na2 Si1 100.94(7) . 2
Si1 Na2 Si1 53.60(4) 9 2
Si1 Na2 Si1 180.00(5) 10 2
O3 Na2 Si1 88.59(13) . 12
O3 Na2 Si1 91.41(13) 9 12
O3 Na2 Si1 153.15(2) 11 12
O3 Na2 Si1 26.85(2) 3 12
O1 Na2 Si1 78.21(7) 9 12
O1 Na2 Si1 26.90(7) 12 12
O1 Na2 Si1 153.10(7) 4 12
O1 Na2 Si1 100.94(7) 11 12
O1 Na2 Si1 79.06(7) 3 12
O1 Na2 Si1 60.15(7) 10 12
O1 Na2 Si1 119.85(7) 2 12
O1 Na2 Si1 101.79(7) . 12
Si1 Na2 Si1 78.269(18) 9 12
Si1 Na2 Si1 78.269(18) 10 12
Si1 Na2 Si1 101.731(18) 2 12
O1 U1 O1 142.80(18) 2 7
O1 U1 O1 73.25(9) 2 3
O1 U1 O1 141.86(18) 7 3
O1 U1 O1 141.86(18) 2 5
O1 U1 O1 73.25(9) 7 5
O1 U1 O1 77.28(19) 3 5
O1 U1 O1 77.28(19) 2 8
O1 U1 O1 115.06(19) 7 8
O1 U1 O1 77.87(18) 3 8
O1 U1 O1 73.25(9) 5 8
O1 U1 O1 77.87(18) 2 6
O1 U1 O1 73.25(9) 7 6
O1 U1 O1 142.80(18) 3 6
O1 U1 O1 115.06(19) 5 6
O1 U1 O1 73.25(9) 8 6
O1 U1 O1 73.25(9) 2 4
O1 U1 O1 77.87(18) 7 4
O1 U1 O1 115.06(19) 3 4
O1 U1 O1 142.80(18) 5 4
O1 U1 O1 141.86(18) 8 4
O1 U1 O1 77.28(19) 6 4
O1 U1 O1 115.06(19) 2 .
O1 U1 O1 77.28(19) 7 .
O1 U1 O1 73.25(9) 3 .
O1 U1 O1 77.87(18) 5 .
O1 U1 O1 142.80(18) 8 .
O1 U1 O1 141.86(18) 6 .
O1 U1 O1 73.25(9) 4 .
O1 U1 Ca1 38.94(9) 2 1_545
O1 U1 Ca1 109.07(9) 7 1_545
O1 U1 Ca1 109.07(9) 3 1_545
O1 U1 Ca1 141.06(9) 5 1_545
O1 U1 Ca1 70.93(9) 8 1_545
O1 U1 Ca1 38.94(9) 6 1_545
O1 U1 Ca1 70.93(9) 4 1_545
O1 U1 Ca1 141.06(9) . 1_545
O1 U1 Na1 70.93(9) 2 3
O1 U1 Na1 141.06(9) 7 3
O1 U1 Na1 38.94(9) 3 3
O1 U1 Na1 70.93(9) 5 3
O1 U1 Na1 38.94(9) 8 3
O1 U1 Na1 109.07(9) 6 3
O1 U1 Na1 141.06(9) 4 3
O1 U1 Na1 109.07(9) . 3
Ca1 U1 Na1 90.0 1_545 3
O1 U1 Na1 109.07(9) 2 3_655
O1 U1 Na1 38.94(9) 7 3_655
O1 U1 Na1 141.06(9) 3 3_655
O1 U1 Na1 109.07(9) 5 3_655
O1 U1 Na1 141.06(9) 8 3_655
O1 U1 Na1 70.93(9) 6 3_655
O1 U1 Na1 38.94(9) 4 3_655
O1 U1 Na1 70.93(9) . 3_655
Ca1 U1 Na1 90.0 1_545 3_655
Na1 U1 Na1 180.0 3 3_655
O1 Si1 O2 114.3(2) . .
O1 Si1 O3 110.4(3) . .
O2 Si1 O3 108.0(3) . .
O1 Si1 O2 105.2(2) . 4_565
O2 Si1 O2 108.3(3) . 4_565
O3 Si1 O2 110.6(3) . 4_565
O1 Si1 Ca1 48.04(14) . .
O2 Si1 Ca1 123.91(15) . .
O3 Si1 Ca1 128.0(2) . .
O2 Si1 Ca1 57.24(14) 4_565 .
O1 Si1 Na2 65.23(15) . .
O2 Si1 Na2 110.41(16) . .
O3 Si1 Na2 49.1(2) . .
O2 Si1 Na2 140.48(16) 4_565 .
Ca1 Si1 Na2 105.06(4) . .
Si1 O1 U1 147.8(2) . .
Si1 O1 Ca1 102.74(19) . .
U1 O1 Ca1 103.04(13) . .
Si1 O1 Na2 87.87(16) . .
U1 O1 Na2 83.58(11) . .
Ca1 O1 Na2 141.97(15) . .
Si1 O2 Si1 148.4(3) . 3_655
Si1 O2 Na1 120.16(19) . 3_655
Si1 O2 Na1 91.43(17) 3_655 3_655
Si1 O2 Ca1 120.16(19) . 3_655
Si1 O2 Ca1 91.43(17) 3_655 3_655
Na1 O2 Ca1 0.0 3_655 3_655
Si1 O2 Na2 49.07(12) . .
Si1 O2 Na2 133.47(18) 3_655 .
Na1 O2 Na2 95.18(10) 3_655 .
Ca1 O2 Na2 95.18(10) 3_655 .
Si1 O3 Si1 151.2(5) . 10
Si1 O3 Na2 104.1(2) . .
Si1 O3 Na2 104.1(2) 10 .
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_distance
_geom_bond_site_symmetry_2
Ca1 O1 2.399(4) .
Ca1 O1 2.399(4) 6_565
Ca1 O1 2.399(4) 5
Ca1 O1 2.399(4) 2_565
Ca1 O2 2.647(4) 3
Ca1 O2 2.647(4) 7
Ca1 O2 2.647(4) 8_565
Ca1 O2 2.647(4) 4_565
Ca1 Si1 3.1467(14) 6_565
Ca1 Si1 3.1467(14) 2_565
Ca1 Si1 3.1467(14) 5
Ca1 Si1 3.1467(14) .
Na2 O3 2.710(7) .
Na2 O3 2.710(7) 9
Na2 O3 2.710(7) 11
Na2 O3 2.710(7) 3
Na2 O1 3.160(4) 9
Na2 O1 3.160(4) 12
Na2 O1 3.160(4) 4
Na2 O1 3.160(4) 11
Na2 O1 3.160(4) 3
Na2 O1 3.160(4) 10
Na2 O1 3.160(4) 2
Na2 O1 3.160(4) .
Na2 Si1 3.4778(15) 9
Na2 Si1 3.4778(15) 10
Na2 Si1 3.4778(15) 2
Na2 Si1 3.4778(15) 12
U1 O1 2.351(4) 2
U1 O1 2.351(4) 7
U1 O1 2.351(4) 3
U1 O1 2.351(4) 5
U1 O1 2.351(4) 8
U1 O1 2.351(4) 6
U1 O1 2.351(4) 4
U1 O1 2.351(4) .
U1 Ca1 3.7190(8) 1_545
U1 Na1 3.7190(8) 3
U1 Na1 3.7190(8) 3_655
Si1 O1 1.575(4) .
Si1 O2 1.614(4) .
Si1 O3 1.619(2) .
Si1 O2 1.637(4) 4_565
O2 Si1 1.637(4) 3_655
O2 Na1 2.647(4) 3_655
O2 Ca1 2.647(4) 3_655
O3 Si1 1.619(2) 10