#$Date: 2022-03-06 06:37:54 +0200 (Sun, 06 Mar 2022) $
#$Revision: 273468 $
#$URL: file:///home/coder/svn-repositories/cod/cif/1/56/59/1565962.cif $
#------------------------------------------------------------------------------
#
# This file is available in the Crystallography Open Database (COD),
# http://www.crystallography.net/
#
# All data on this site have been placed in the public domain by the
# contributors.
#
data_1565962
loop_
_publ_author_name
'Wildner, Manfred'
'Zakharov, Boris A.'
'Bogdanov, Nikita E.'
'Talla, Dominik'
'Boldyreva, Elena V.'
'Miletich, Ronald'
_publ_section_title
;
 Crystallography relevant to Mars and Galilean icy moons: crystal behavior
 of kieserite-type monohydrate sulfates at extraterrestrial conditions
 down to 15 K
;
_journal_issue                   2
_journal_name_full               IUCrJ
_journal_page_first              194
_journal_page_last               203
_journal_paper_doi               10.1107/S2052252521012720
_journal_volume                  9
_journal_year                    2022
_chemical_formula_sum            'H2 Ni O5 S'
_chemical_formula_weight         172.79
_space_group_crystal_system      monoclinic
_space_group_IT_number           15
_space_group_name_Hall           '-C 2yc'
_space_group_name_H-M_alt        'C 1 2/c 1'
_atom_sites_solution_hydrogens   difmap
_audit_creation_method           SHELXL-2017/1
_cell_angle_alpha                90
_cell_angle_beta                 117.580(10)
_cell_angle_gamma                90
_cell_formula_units_Z            4
_cell_length_a                   6.8037(10)
_cell_length_b                   7.6178(10)
_cell_length_c                   7.4371(10)
_cell_measurement_temperature    113(2)
_cell_volume                     341.66(9)
_computing_structure_refinement  'SHELXL-2017/1 (Sheldrick, 2017)'
_diffrn_ambient_temperature      113(2)
_diffrn_measured_fraction_theta_full 1.000
_diffrn_measured_fraction_theta_max 1.000
_diffrn_radiation_type           MoK\a
_diffrn_radiation_wavelength     0.71073
_diffrn_reflns_av_R_equivalents  0.0235
_diffrn_reflns_av_unetI/netI     0.0105
_diffrn_reflns_Laue_measured_fraction_full 1.000
_diffrn_reflns_Laue_measured_fraction_max 1.000
_diffrn_reflns_limit_h_max       12
_diffrn_reflns_limit_h_min       -12
_diffrn_reflns_limit_k_max       13
_diffrn_reflns_limit_k_min       -13
_diffrn_reflns_limit_l_max       13
_diffrn_reflns_limit_l_min       -13
_diffrn_reflns_number            10699
_diffrn_reflns_point_group_measured_fraction_full 1.000
_diffrn_reflns_point_group_measured_fraction_max 1.000
_diffrn_reflns_theta_full        25.242
_diffrn_reflns_theta_max         39.975
_diffrn_reflns_theta_min         4.297
_exptl_absorpt_coefficient_mu    6.165
_exptl_absorpt_correction_T_max  0.7479
_exptl_absorpt_correction_T_min  0.6624
_exptl_absorpt_correction_type   multi-scan
_exptl_absorpt_process_details
;
 SADABS 2016/2: Krause, L., Herbst-Irmer, R., Sheldrick G.M. & Stalke D.,
 J. Appl. Cryst. 48 (2015) 3-10
;
_exptl_crystal_density_diffrn    3.359
_exptl_crystal_F_000             344
_refine_diff_density_max         0.825
_refine_diff_density_min         -0.666
_refine_diff_density_rms         0.124
_refine_ls_extinction_coef       0.0186(13)
_refine_ls_extinction_expression Fc^*^=kFc[1+0.001xFc²λ³/sin(2θ)]^-1/4^
_refine_ls_extinction_method     'SHELXL-2017/1 (Sheldrick 2017)'
_refine_ls_goodness_of_fit_ref   1.123
_refine_ls_hydrogen_treatment    refall
_refine_ls_matrix_type           full
_refine_ls_number_parameters     40
_refine_ls_number_reflns         1061
_refine_ls_number_restraints     0
_refine_ls_restrained_S_all      1.123
_refine_ls_R_factor_all          0.0166
_refine_ls_R_factor_gt           0.0161
_refine_ls_shift/su_max          0.000
_refine_ls_shift/su_mean         0.000
_refine_ls_structure_factor_coef Fsqd
_refine_ls_weighting_details
'w=1/[σ²(Fo²)+(0.0210P)²+0.5300P] where P=(Fo²+2Fc²)/3'
_refine_ls_weighting_scheme      calc
_refine_ls_wR_factor_gt          0.0419
_refine_ls_wR_factor_ref         0.0422
_reflns_Friedel_coverage         0.000
_reflns_number_gt                1034
_reflns_number_total             1061
_reflns_threshold_expression     'I > 2σ(I)'
_cod_data_source_file            lt5044.cif
_cod_data_source_block           NiSO4H2O_N2_113K
_cod_depositor_comments
'Adding full bibliography for 1565934--1565967.cif.'
_cod_original_sg_symbol_H-M      'C 2/c'
_cod_database_code               1565962
_shelx_shelxl_version_number     2017/1
_shelx_space_group_comment
;
The symmetry employed for this shelxl refinement is uniquely defined
by the following loop, which should always be used as a source of
symmetry information in preference to the above space-group names.
They are only intended as comments.
;
loop_
_space_group_symop_operation_xyz
'x, y, z'
'-x, y, -z+1/2'
'x+1/2, y+1/2, z'
'-x+1/2, y+1/2, -z+1/2'
'-x, -y, -z'
'x, -y, z-1/2'
'-x+1/2, -y+1/2, -z'
'x+1/2, -y+1/2, z-1/2'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_adp_type
_atom_site_occupancy
_atom_site_site_symmetry_order
_atom_site_calc_flag
_atom_site_refinement_flags_posn
_atom_site_refinement_flags_adp
_atom_site_refinement_flags_occupancy
_atom_site_disorder_assembly
_atom_site_disorder_group
Ni Ni 0.000000 0.500000 0.000000 0.00292(5) Uani 1 2 d S . P . .
S S 0.000000 0.15763(4) 0.250000 0.00284(5) Uani 1 2 d S T P . .
O1 O 0.17257(10) 0.04772(9) 0.40473(9) 0.00604(10) Uani 1 1 d . . . . .
O2 O 0.10507(10) 0.27108(8) 0.15552(9) 0.00506(9) Uani 1 1 d . . . . .
O3 O 0.000000 0.63055(12) 0.250000 0.00491(12) Uani 1 2 d S T P . .
H H 0.109(3) 0.695(3) 0.294(3) 0.020(5) Uiso 1 1 d . . . . .
loop_
_atom_type_symbol
_atom_type_description
_atom_type_scat_dispersion_real
_atom_type_scat_dispersion_imag
_atom_type_scat_source
O O 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
H H 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
S S 0.1246 0.1234 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Ni Ni 0.3393 1.1124 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
_geom_angle_publ_flag
O2 Ni O2 180.0 . 5_565 ?
O2 Ni O1 94.87(3) . 8_455 ?
O2 Ni O1 85.13(3) 5_565 8_455 ?
O2 Ni O1 85.13(3) . 4 ?
O2 Ni O1 94.87(3) 5_565 4 ?
O1 Ni O1 180.0 8_455 4 ?
O2 Ni O3 87.33(3) . 5_565 ?
O2 Ni O3 92.67(3) 5_565 5_565 ?
O1 Ni O3 93.19(2) 8_455 5_565 ?
O1 Ni O3 86.81(2) 4 5_565 ?
O2 Ni O3 92.67(3) . . ?
O2 Ni O3 87.33(3) 5_565 . ?
O1 Ni O3 86.81(2) 8_455 . ?
O1 Ni O3 93.19(2) 4 . ?
O3 Ni O3 180.0 5_565 . ?
O2 Ni O2 81.681(14) . 8_455 ?
O2 Ni O2 98.320(15) 5_565 8_455 ?
O1 Ni O2 43.64(2) 8_455 8_455 ?
O1 Ni O2 136.36(2) 4 8_455 ?
O3 Ni O2 51.304(16) 5_565 8_455 ?
O3 Ni O2 128.696(16) . 8_455 ?
O2 Ni O2 98.320(14) . 4 ?
O2 Ni O2 81.680(15) 5_565 4 ?
O1 Ni O2 136.36(2) 8_455 4 ?
O1 Ni O2 43.64(2) 4 4 ?
O3 Ni O2 128.696(16) 5_565 4 ?
O3 Ni O2 51.304(16) . 4 ?
O2 Ni O2 180.00(2) 8_455 4 ?
O2 Ni O2 136.09(2) . 6_565 ?
O2 Ni O2 43.91(2) 5_565 6_565 ?
O1 Ni O2 113.79(2) 8_455 6_565 ?
O1 Ni O2 66.21(2) 4 6_565 ?
O3 Ni O2 59.81(3) 5_565 6_565 ?
O3 Ni O2 120.19(3) . 6_565 ?
O2 Ni O2 96.345(19) 8_455 6_565 ?
O2 Ni O2 83.655(18) 4 6_565 ?
O2 Ni O2 43.91(2) . 2 ?
O2 Ni O2 136.09(2) 5_565 2 ?
O1 Ni O2 66.21(2) 8_455 2 ?
O1 Ni O2 113.79(2) 4 2 ?
O3 Ni O2 120.19(3) 5_565 2 ?
O3 Ni O2 59.81(3) . 2 ?
O2 Ni O2 83.655(19) 8_455 2 ?
O2 Ni O2 96.345(18) 4 2 ?
O2 Ni O2 180.000(12) 6_565 2 ?
O1 S O1 110.41(6) 2 . ?
O1 S O2 108.46(4) 2 2 ?
O1 S O2 110.23(4) . 2 ?
O1 S O2 110.23(4) 2 . ?
O1 S O2 108.46(4) . . ?
O2 S O2 109.04(5) 2 . ?
S O1 Ni 136.47(4) . 4_545 ?
S O1 O2 36.07(2) . . ?
Ni O1 O2 100.54(3) 4_545 . ?
S O1 O1 34.80(3) . 2 ?
Ni O1 O1 139.35(4) 4_545 2 ?
O2 O1 O1 60.57(3) . 2 ?
S O1 O2 35.18(2) . 2 ?
Ni O1 O2 145.47(4) 4_545 2 ?
O2 O1 O2 60.36(3) . 2 ?
O1 O1 O2 59.48(2) 2 2 ?
S O1 O2 127.63(4) . 4_545 ?
Ni O1 O2 47.393(19) 4_545 4_545 ?
O2 O1 O2 109.93(3) . 4_545 ?
O1 O1 O2 102.17(3) 2 4_545 ?
O2 O1 O2 161.46(4) 2 4_545 ?
S O1 O3 170.96(4) . 7_556 ?
Ni O1 O3 47.692(15) 4_545 7_556 ?
O2 O1 O3 145.62(3) . 7_556 ?
O1 O1 O3 150.59(2) 2 7_556 ?
O2 O1 O3 135.95(3) 2 7_556 ?
O2 O1 O3 61.41(2) 4_545 7_556 ?
S O1 O2 115.11(4) . 8_556 ?
Ni O1 O2 42.530(19) 4_545 8_556 ?
O2 O1 O2 86.31(2) . 8_556 ?
O1 O1 O2 146.85(3) 2 8_556 ?
O2 O1 O2 104.39(3) 2 8_556 ?
O2 O1 O2 89.92(3) 4_545 8_556 ?
O3 O1 O2 61.64(2) 7_556 8_556 ?
S O1 O3 92.62(3) . 3_545 ?
Ni O1 O3 44.385(17) 4_545 3_545 ?
O2 O1 O3 57.77(2) . 3_545 ?
O1 O1 O3 101.62(4) 2 3_545 ?
O2 O1 O3 115.68(3) 2 3_545 ?
O2 O1 O3 62.47(3) 4_545 3_545 ?
O3 O1 O3 92.08(2) 7_556 3_545 ?
O2 O1 O3 56.87(2) 8_556 3_545 ?
S O1 O2 112.47(4) . 7_556 ?
Ni O1 O2 78.37(2) 4_545 7_556 ?
O2 O1 O2 108.27(3) . 7_556 ?
O1 O1 O2 139.83(3) 2 7_556 ?
O2 O1 O2 81.14(2) 2 7_556 ?
O2 O1 O2 117.40(3) 4_545 7_556 ?
O3 O1 O2 58.89(2) 7_556 7_556 ?
O2 O1 O2 45.85(2) 8_556 7_556 ?
O3 O1 O2 102.49(2) 3_545 7_556 ?
S O1 O2 127.40(4) . 6_556 ?
Ni O1 O2 95.18(3) 4_545 6_556 ?
O2 O1 O2 162.63(4) . 6_556 ?
O1 O1 O2 102.46(3) 2 6_556 ?
O2 O1 O2 109.16(3) 2 6_556 ?
O2 O1 O2 75.71(3) 4_545 6_556 ?
O3 O1 O2 51.68(2) 7_556 6_556 ?
O2 O1 O2 110.45(3) 8_556 6_556 ?
O3 O1 O2 135.11(3) 3_545 6_556 ?
O2 O1 O2 81.988(19) 7_556 6_556 ?
S O1 O1 89.57(3) . 5_556 ?
Ni O1 O1 133.31(4) 4_545 5_556 ?
O2 O1 O1 124.21(4) . 5_556 ?
O1 O1 O1 80.76(3) 2 5_556 ?
O2 O1 O1 65.81(3) 2 5_556 ?
O2 O1 O1 116.79(4) 4_545 5_556 ?
O3 O1 O1 85.62(3) 7_556 5_556 ?
O2 O1 O1 121.19(3) 8_556 5_556 ?
O3 O1 O1 177.60(3) 3_545 5_556 ?
O2 O1 O1 75.73(3) 7_556 5_556 ?
O2 O1 O1 43.355(19) 6_556 5_556 ?
S O2 Ni 130.38(4) . . ?
S O2 O1 35.47(2) . . ?
Ni O2 O1 160.09(4) . . ?
S O2 O2 35.48(3) . 2 ?
Ni O2 O2 100.58(2) . 2 ?
O1 O2 O2 60.36(3) . 2 ?
S O2 O1 34.59(2) . 2 ?
Ni O2 O1 117.30(3) . 2 ?
O1 O2 O1 59.94(3) . 2 ?
O2 O2 O1 59.28(2) 2 2 ?
S O2 O3 106.74(4) . 3_545 ?
Ni O2 O3 122.74(3) . 3_545 ?
O1 O2 O3 72.69(3) . 3_545 ?
O2 O2 O3 129.78(3) 2 3_545 ?
O1 O2 O3 111.76(3) 2 3_545 ?
S O2 O1 160.48(4) . 4 ?
Ni O2 O1 47.48(2) . 4 ?
O1 O2 O1 138.31(3) . 4 ?
O2 O2 O1 127.67(2) 2 4 ?
O1 O2 O1 161.46(4) 2 4 ?
O3 O2 O1 77.72(3) 3_545 4 ?
S O2 O3 135.23(4) . 5_565 ?
Ni O2 O3 47.46(2) . 5_565 ?
O1 O2 O3 150.01(4) . 5_565 ?
O2 O2 O3 133.23(4) 2 5_565 ?
O1 O2 O3 101.31(3) 2 5_565 ?
O3 O2 O3 96.46(2) 3_545 5_565 ?
O1 O2 O3 60.97(2) 4 5_565 ?
S O2 O1 90.77(3) . 8_455 ?
Ni O2 O1 42.600(17) . 8_455 ?
O1 O2 O1 126.15(4) . 8_455 ?
O2 O2 O1 71.81(3) 2 8_455 ?
O1 O2 O1 75.61(3) 2 8_455 ?
O3 O2 O1 158.30(3) 3_545 8_455 ?
O1 O2 O1 90.08(3) 4 8_455 ?
O3 O2 O1 61.85(2) 5_565 8_455 ?
S O2 O3 101.60(3) . . ?
Ni O2 O3 44.693(16) . . ?
O1 O2 O3 116.65(3) . . ?
O2 O2 O3 66.120(14) 2 . ?
O1 O2 O3 115.77(3) 2 . ?
O3 O2 O3 128.76(3) 3_545 . ?
O1 O2 O3 63.03(2) 4 . ?
O3 O2 O3 92.15(2) 5_565 . ?
O1 O2 O3 56.769(17) 8_455 . ?
S O2 O1 82.62(3) . 7_556 ?
Ni O2 O1 94.97(3) . 7_556 ?
O1 O2 O1 71.73(3) . 7_556 ?
O2 O2 O1 62.34(3) 2 7_556 ?
O1 O2 O1 116.70(3) 2 7_556 ?
O3 O2 O1 87.83(2) 3_545 7_556 ?
O1 O2 O1 78.53(2) 4 7_556 ?
O3 O2 O1 137.03(3) 5_565 7_556 ?
O1 O2 O1 107.46(3) 8_455 7_556 ?
O3 O2 O1 54.477(17) . 7_556 ?
S O2 O1 93.67(3) . 6 ?
Ni O2 O1 115.12(3) . 6 ?
O1 O2 O1 83.40(2) . 6 ?
O2 O2 O1 128.01(2) 2 6 ?
O1 O2 O1 70.84(3) 2 6 ?
O3 O2 O1 56.88(2) 3_545 6 ?
O1 O2 O1 104.29(3) 4 6 ?
O3 O2 O1 67.66(3) 5_565 6 ?
O1 O2 O1 110.45(3) 8_455 6 ?
O3 O2 O1 159.81(3) . 6 ?
O1 O2 O1 141.95(2) 7_556 6 ?
Ni O3 Ni 123.72(4) . 2 ?
Ni O3 O2 111.614(17) . 3_455 ?
Ni O3 O2 90.591(16) 2 3_455 ?
Ni O3 O2 90.591(16) . 4 ?
Ni O3 O2 111.614(17) 2 4 ?
O2 O3 O2 132.67(5) 3_455 4 ?
Ni O3 O1 45.499(17) . 8_455 ?
Ni O3 O1 104.53(3) 2 8_455 ?
O2 O3 O1 71.43(2) 3_455 8_455 ?
O2 O3 O1 134.54(2) 4 8_455 ?
Ni O3 O1 104.53(3) . 7_556 ?
Ni O3 O1 45.499(17) 2 7_556 ?
O2 O3 O1 134.54(2) 3_455 7_556 ?
O2 O3 O1 71.43(2) 4 7_556 ?
O1 O3 O1 123.01(4) 8_455 7_556 ?
Ni O3 O2 162.15(3) . 6_566 ?
Ni O3 O2 45.207(15) 2 6_566 ?
O2 O3 O2 84.38(2) 3_455 6_566 ?
O2 O3 O2 83.54(2) 4 6_566 ?
O1 O3 O2 141.79(2) 8_455 6_566 ?
O1 O3 O2 57.62(2) 7_556 6_566 ?
Ni O3 O2 45.207(15) . 5_565 ?
Ni O3 O2 162.15(3) 2 5_565 ?
O2 O3 O2 83.54(2) 3_455 5_565 ?
O2 O3 O2 84.38(2) 4 5_565 ?
O1 O3 O2 57.62(2) 8_455 5_565 ?
O1 O3 O2 141.79(2) 7_556 5_565 ?
O2 O3 O2 149.60(4) 6_566 5_565 ?
Ni O3 O2 42.641(19) . . ?
Ni O3 O2 82.71(3) 2 . ?
O2 O3 O2 128.76(3) 3_455 . ?
O2 O3 O2 96.202(18) 4 . ?
O1 O3 O2 61.59(2) 8_455 . ?
O1 O3 O2 66.63(3) 7_556 . ?
O2 O3 O2 121.13(3) 6_566 . ?
O2 O3 O2 87.85(2) 5_565 . ?
Ni O3 O2 82.71(3) . 2 ?
Ni O3 O2 42.641(19) 2 2 ?
O2 O3 O2 96.202(17) 3_455 2 ?
O2 O3 O2 128.76(3) 4 2 ?
O1 O3 O2 66.63(3) 8_455 2 ?
O1 O3 O2 61.59(2) 7_556 2 ?
O2 O3 O2 87.85(2) 6_566 2 ?
O2 O3 O2 121.13(3) 5_565 2 ?
O2 O3 O2 47.76(3) . 2 ?
Ni O3 O1 122.71(3) . 3_455 ?
Ni O3 O1 42.424(14) 2 3_455 ?
O2 O3 O1 49.536(19) 3_455 3_455 ?
O2 O3 O1 144.81(2) 4 3_455 ?
O1 O3 O1 80.57(2) 8_455 3_455 ?
O1 O3 O1 87.92(2) 7_556 3_455 ?
O2 O3 O1 61.28(2) 6_566 3_455 ?
O2 O3 O1 126.19(2) 5_565 3_455 ?
O2 O3 O1 101.38(3) . 3_455 ?
O2 O3 O1 54.50(2) 2 3_455 ?
Ni O3 O1 42.424(13) . 4 ?
Ni O3 O1 122.71(3) 2 4 ?
O2 O3 O1 144.81(2) 3_455 4 ?
O2 O3 O1 49.536(19) 4 4 ?
O1 O3 O1 87.92(2) 8_455 4 ?
O1 O3 O1 80.57(2) 7_556 4 ?
O2 O3 O1 126.192(19) 6_566 4 ?
O2 O3 O1 61.28(2) 5_565 4 ?
O2 O3 O1 54.50(2) . 4 ?
O2 O3 O1 101.38(3) 2 4 ?
O1 O3 O1 155.80(4) 3_455 4 ?
Ni O3 H 105.3(15) . . ?
Ni O3 H 107.3(15) 2 . ?
O2 O3 H 118.9(15) 3_455 . ?
O2 O3 H 16.1(15) 4 . ?
O1 O3 H 146.2(15) 8_455 . ?
O1 O3 H 74.7(15) 7_556 . ?
O2 O3 H 71.6(15) 6_566 . ?
O2 O3 H 90.3(15) 5_565 . ?
O2 O3 H 111.5(15) . . ?
O2 O3 H 136.1(15) 2 . ?
O1 O3 H 131.8(15) 3_455 . ?
O1 O3 H 65.4(15) 4 . ?
Ni O3 H 107.3(15) . 2 ?
Ni O3 H 105.3(15) 2 2 ?
O2 O3 H 16.1(15) 3_455 2 ?
O2 O3 H 118.9(15) 4 2 ?
O1 O3 H 74.7(15) 8_455 2 ?
O1 O3 H 146.2(15) 7_556 2 ?
O2 O3 H 90.3(15) 6_566 2 ?
O2 O3 H 71.6(15) 5_565 2 ?
O2 O3 H 136.1(15) . 2 ?
O2 O3 H 111.5(15) 2 2 ?
O1 O3 H 65.4(15) 3_455 2 ?
O1 O3 H 131.8(15) 4 2 ?
H O3 H 107(3) . 2 ?
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_distance
_geom_bond_site_symmetry_2
_geom_bond_publ_flag
Ni O2 2.0309(6) . ?
Ni O2 2.0309(6) 5_565 ?
Ni O1 2.0336(7) 8_455 ?
Ni O1 2.0336(7) 4 ?
Ni O3 2.1085(5) 5_565 ?
Ni O3 2.1085(5) . ?
Ni O2 3.4166(7) 8_455 ?
Ni O2 3.4166(7) 4 ?
Ni O2 3.4368(7) 6_565 ?
Ni O2 3.4368(7) 2 ?
S O1 1.4672(7) 2 ?
S O1 1.4672(7) . ?
S O2 1.4888(6) 2 ?
S O2 1.4888(6) . ?
O1 O2 2.3985(9) . ?
O1 O1 2.4097(13) 2 ?
O1 O2 2.4249(9) 2 ?
O1 O2 2.7493(9) 4_545 ?
O1 O3 2.8467(8) 7_556 ?
O1 O2 2.9935(10) 8_556 ?
O1 O3 3.0098(7) 3_545 ?
O1 O2 3.2108(10) 7_556 ?
O1 O2 3.2219(9) 6_556 ?
O1 O1 3.3365(13) 5_556 ?
O2 O2 2.4247(12) 2 ?
O2 O3 2.6667(8) 3_545 ?
O2 O3 2.8587(8) 5_565 ?
O2 O3 2.9948(11) . ?
O3 H 0.82(2) . ?
O3 H 0.82(2) 2 ?
loop_
_geom_hbond_atom_site_label_D
_geom_hbond_atom_site_label_H
_geom_hbond_atom_site_label_A
_geom_hbond_distance_DH
_geom_hbond_distance_HA
_geom_hbond_distance_DA
_geom_hbond_angle_DHA
_geom_hbond_site_symmetry_A
_geom_hbond_publ_flag
O3 H O2 0.82(2) 1.89(2) 2.6667(8) 157(2) 4 yes