data_8102639
loop_
_publ_author_name
'Li-Hui Zhang'
'Jin Yang'
_publ_section_title
;
 Crystal structure of
 3,3'-(butane-1,4-diyl)bis(2-ethylbenzimidazole)-1-ium-(m6-oxo)-dodecakis(m2-oxo)-hexaoxohexamolybdenum(VI),
 [C22H28N4][Mo6O19]
;
_journal_issue                   1
_journal_name_full
'Zeitschrift für Kristallographie - New Crystal Structures'
_journal_page_first              201
_journal_volume                  225
_journal_year                    2010
_chemical_formula_moiety         'C22 H28 N4, Mo6 O19'
_chemical_formula_sum            'C22 H28 Mo6 N4 O19'
_chemical_formula_weight         1228.12
_chemical_melting_point          ?
_chemical_name_common
;
Bis[3,3'-(butane-1,4-diyl)bis(2-ethylbenzimidazole)-1-ium] 
hexamolybdate(VI)
;
_chemical_name_systematic
;
Bis[3,3'-(butane-1,4-diyl)bis(2-ethylbenzimidazole)-1-ium] hexamolybdate(VI)
;
_space_group_IT_number           2
_symmetry_cell_setting           triclinic
_symmetry_space_group_name_Hall  '-P 1'
_symmetry_space_group_name_H-M   'P -1'
_atom_sites_solution_hydrogens   geom
_atom_sites_solution_primary     direct
_atom_sites_solution_secondary   difmap
_audit_creation_method           SHELXL-97
_cell_angle_alpha                100.267(7)
_cell_angle_beta                 96.232(7)
_cell_angle_gamma                107.605(8)
_cell_formula_units_Z            1
_cell_length_a                   7.8136(8)
_cell_length_b                   10.4120(9)
_cell_length_c                   10.8054(9)
_cell_measurement_reflns_used    3711
_cell_measurement_temperature    293(2)
_cell_measurement_theta_max      26
_cell_measurement_theta_min      2
_cell_volume                     812.02(14)
_computing_cell_refinement       CrysAlis
_computing_data_collection       'CrysAlis [4]'
_computing_data_reduction        CrysAlis
_computing_structure_refinement  'SHELXL-97 [6]'
_computing_structure_solution    'SHELXS-97 [5]'
_diffrn_ambient_temperature      293(2)
_diffrn_detector_area_resol_mean 10.0
_diffrn_measured_fraction_theta_full 0.993
_diffrn_measured_fraction_theta_max 0.833
_diffrn_measurement_device_type  'Oxford Diffraction Gemini R Ultra'
_diffrn_measurement_method       'ω scan'
_diffrn_radiation_monochromator  graphite
_diffrn_radiation_source         'fine-focus sealed tube'
_diffrn_radiation_type           MoK\a
_diffrn_radiation_wavelength     0.71073
_diffrn_reflns_av_R_equivalents  0.0201
_diffrn_reflns_av_sigmaI/netI    0.0542
_diffrn_reflns_limit_h_max       9
_diffrn_reflns_limit_h_min       -8
_diffrn_reflns_limit_k_max       13
_diffrn_reflns_limit_k_min       -12
_diffrn_reflns_limit_l_max       13
_diffrn_reflns_limit_l_min       -12
_diffrn_reflns_number            5807
_diffrn_reflns_theta_full        25.00
_diffrn_reflns_theta_max         29.33
_diffrn_reflns_theta_min         3.17
_exptl_absorpt_coefficient_mu    2.336
_exptl_absorpt_correction_T_max  0.890
_exptl_absorpt_correction_T_min  0.765
_exptl_absorpt_correction_type   empirical
_exptl_absorpt_process_details
;
Oxford Diffraction: CrysAlis [4].
;
_exptl_crystal_colour            Green
_exptl_crystal_density_diffrn    2.511
_exptl_crystal_density_method    'not measured'
_exptl_crystal_description       block
_exptl_crystal_F_000             592
_exptl_crystal_size_max          0.20
_exptl_crystal_size_mid          0.10
_exptl_crystal_size_min          0.05
_refine_diff_density_max         0.424
_refine_diff_density_min         -0.490
_refine_diff_density_rms         0.096
_refine_ls_extinction_method     none
_refine_ls_goodness_of_fit_ref   0.836
_refine_ls_hydrogen_treatment    constr
_refine_ls_matrix_type           full
_refine_ls_number_parameters     232
_refine_ls_number_reflns         3711
_refine_ls_number_restraints     0
_refine_ls_restrained_S_all      0.836
_refine_ls_R_factor_all          0.0400
_refine_ls_R_factor_gt           0.0260
_refine_ls_shift/su_max          0.001
_refine_ls_shift/su_mean         0.000
_refine_ls_structure_factor_coef Fsqd
_refine_ls_weighting_details
'calc w=1/[σ²(Fo²)+(0.0178P)²+0.0000P] where P=(Fo²+2Fc²)/3'
_refine_ls_weighting_scheme      calc
_refine_ls_wR_factor_gt          0.0451
_refine_ls_wR_factor_ref         0.0467
_reflns_number_gt                2735
_reflns_number_total             3711
_reflns_threshold_expression     >2sigma(I)
_cod_data_source_file            1267-2883.cff
_cod_data_source_block           a
_cod_depositor_comments
;
The following automatic conversions were performed:

'_chemical_melting_point' value 'not measured' was changed to '?' -
the value is undefined or not given.

Automatic conversion script
Id: cif_fix_values 1569 2011-02-09 13:29:24Z adriana 
;
_cod_original_cell_volume        812.02(13)
_cod_database_code               8102639
loop_
_symmetry_equiv_pos_as_xyz
'x, y, z'
'-x, -y, -z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_adp_type
_atom_site_occupancy
_atom_site_symmetry_multiplicity
_atom_site_calc_flag
_atom_site_refinement_flags
_atom_site_disorder_assembly
_atom_site_disorder_group
Mo1 Mo 0.91195(4) 0.47399(3) 0.69437(2) 0.03249(9) Uani 1 1 d . . .
Mo2 Mo 1.30294(4) 0.58486(3) 0.59858(3) 0.03101(9) Uani 1 1 d . . .
Mo3 Mo 1.01695(4) 0.27887(3) 0.46199(3) 0.02787(8) Uani 1 1 d . . .
C1 C 0.4195(6) 1.0998(4) -0.4028(3) 0.0577(12) Uani 1 1 d . . .
H1A H 0.4389 1.1488 -0.4701 0.087 Uiso 1 1 calc R . .
H1B H 0.3294 1.0103 -0.4360 0.087 Uiso 1 1 calc R . .
H1C H 0.5319 1.0891 -0.3687 0.087 Uiso 1 1 calc R . .
C2 C 0.3548(6) 1.1794(4) -0.2993(3) 0.0547(11) Uani 1 1 d . . .
H2A H 0.4449 1.2707 -0.2692 0.066 Uiso 1 1 calc R . .
H2B H 0.2427 1.1909 -0.3356 0.066 Uiso 1 1 calc R . .
C3 C 0.3214(4) 1.1161(4) -0.1888(3) 0.0315(8) Uani 1 1 d . . .
C4 C 0.2660(4) 0.9639(3) -0.0657(3) 0.0266(7) Uani 1 1 d . . .
C5 C 0.2333(5) 0.8468(4) -0.0162(3) 0.0350(8) Uani 1 1 d . . .
H5 H 0.2370 0.7638 -0.0627 0.042 Uiso 1 1 calc R . .
C6 C 0.1950(5) 0.8602(4) 0.1057(3) 0.0424(9) Uani 1 1 d . . .
H6 H 0.1732 0.7843 0.1433 0.051 Uiso 1 1 calc R . .
C7 C 0.1880(5) 0.9851(4) 0.1746(3) 0.0439(10) Uani 1 1 d . . .
H7 H 0.1615 0.9897 0.2568 0.053 Uiso 1 1 calc R . .
C8 C 0.2187(5) 1.1010(4) 0.1253(3) 0.0364(9) Uani 1 1 d . . .
H8 H 0.2131 1.1835 0.1716 0.044 Uiso 1 1 calc R . .
C9 C 0.2589(4) 1.0884(3) 0.0022(3) 0.0268(7) Uani 1 1 d . . .
C10 C 0.3022(5) 1.3268(3) -0.0469(3) 0.0381(9) Uani 1 1 d . . .
H10A H 0.2311 1.3394 0.0197 0.046 Uiso 1 1 calc R . .
H10B H 0.2477 1.3485 -0.1220 0.046 Uiso 1 1 calc R . .
C11 C 0.4941(4) 1.4252(3) -0.0032(3) 0.0334(8) Uani 1 1 d . . .
H11A H 0.5709 1.4006 -0.0616 0.040 Uiso 1 1 calc R . .
H11B H 0.5402 1.4160 0.0806 0.040 Uiso 1 1 calc R . .
N1 N 0.3062(4) 0.9873(3) -0.1838(2) 0.0298(6) Uani 1 1 d . . .
H1 H 0.3191 0.9270 -0.2444 0.036 Uiso 1 1 calc R . .
N2 N 0.2946(4) 1.1815(3) -0.0773(2) 0.0289(6) Uani 1 1 d . . .
O1 O 0.9396(3) 0.2958(2) 0.62318(18) 0.0323(5) Uani 1 1 d . . .
O2 O 0.8489(4) 0.4531(3) 0.8350(2) 0.0507(7) Uani 1 1 d . . .
O3 O 0.9197(3) 0.6563(2) 0.69158(18) 0.0282(5) Uani 1 1 d . . .
O4 O 1.1731(3) 0.5422(2) 0.73597(18) 0.0332(6) Uani 1 1 d . . .
O5 O 1.0000 0.5000 0.5000 0.0203(6) Uani 1 2 d S . .
O6 O 1.2332(3) 0.7488(2) 0.61588(18) 0.0283(5) Uani 1 1 d . . .
O7 O 1.5192(3) 0.6451(3) 0.6732(2) 0.0524(8) Uani 1 1 d . . .
O8 O 1.3147(3) 0.5920(2) 0.42341(19) 0.0315(5) Uani 1 1 d . . .
O9 O 1.2556(3) 0.3877(2) 0.54514(18) 0.0309(5) Uani 1 1 d . . .
O10 O 1.0244(3) 0.1172(2) 0.4276(2) 0.0402(6) Uani 1 1 d . . .
loop_
_atom_type_symbol
_atom_type_description
_atom_type_scat_dispersion_real
_atom_type_scat_dispersion_imag
_atom_type_scat_source
C C 0.0033 0.0016 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
H H 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
N N 0.0061 0.0033 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
O O 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Cu Cu 0.3201 1.2651 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Mo Mo -1.6832 0.6857 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
_geom_angle_publ_flag
O2 Mo1 O3 103.29(11) . . ?
O2 Mo1 O4 103.02(11) . . ?
O3 Mo1 O4 87.95(9) . . ?
O2 Mo1 O8 103.81(12) . 2_766 ?
O3 Mo1 O8 88.63(9) . 2_766 ?
O4 Mo1 O8 153.03(9) . 2_766 ?
O2 Mo1 O1 102.97(11) . . ?
O3 Mo1 O1 153.73(9) . . ?
O4 Mo1 O1 85.72(9) . . ?
O8 Mo1 O1 85.62(9) 2_766 . ?
O2 Mo1 O5 179.22(9) . . ?
O3 Mo1 O5 77.48(6) . . ?
O4 Mo1 O5 76.81(6) . . ?
O8 Mo1 O5 76.33(6) 2_766 . ?
O1 Mo1 O5 76.26(6) . . ?
O7 Mo2 O8 105.19(11) . . ?
O7 Mo2 O6 102.95(11) . . ?
O8 Mo2 O6 87.73(9) . . ?
O7 Mo2 O4 101.89(11) . . ?
O8 Mo2 O4 152.91(9) . . ?
O6 Mo2 O4 86.99(9) . . ?
O7 Mo2 O9 103.62(11) . . ?
O8 Mo2 O9 86.65(9) . . ?
O6 Mo2 O9 153.40(9) . . ?
O4 Mo2 O9 86.28(9) . . ?
O7 Mo2 O5 178.47(10) . . ?
O8 Mo2 O5 76.33(6) . . ?
O6 Mo2 O5 77.10(6) . . ?
O4 Mo2 O5 76.58(6) . . ?
O9 Mo2 O5 76.31(6) . . ?
O10 Mo3 O9 104.40(10) . . ?
O10 Mo3 O1 104.36(11) . . ?
O9 Mo3 O1 88.86(9) . . ?
O10 Mo3 O6 101.46(10) . 2_766 ?
O9 Mo3 O6 153.95(9) . 2_766 ?
O1 Mo3 O6 87.74(9) . 2_766 ?
O10 Mo3 O3 101.84(10) . 2_766 ?
O9 Mo3 O3 87.50(9) . 2_766 ?
O1 Mo3 O3 153.64(9) . 2_766 ?
O6 Mo3 O3 84.22(9) 2_766 2_766 ?
O10 Mo3 O5 177.41(7) . . ?
O9 Mo3 O5 77.37(6) . . ?
O1 Mo3 O5 77.47(7) . . ?
O6 Mo3 O5 76.68(6) 2_766 . ?
O3 Mo3 O5 76.25(6) 2_766 . ?
C2 C1 H1A 109.5 . . ?
C2 C1 H1B 109.5 . . ?
H1A C1 H1B 109.5 . . ?
C2 C1 H1C 109.5 . . ?
H1A C1 H1C 109.5 . . ?
H1B C1 H1C 109.5 . . ?
C3 C2 C1 115.2(3) . . ?
C3 C2 H2A 108.5 . . ?
C1 C2 H2A 108.5 . . ?
C3 C2 H2B 108.5 . . ?
C1 C2 H2B 108.5 . . ?
H2A C2 H2B 107.5 . . ?
N1 C3 N2 109.3(3) . . ?
N1 C3 C2 126.5(3) . . ?
N2 C3 C2 124.2(3) . . ?
C5 C4 C9 122.5(3) . . ?
C5 C4 N1 131.7(3) . . ?
C9 C4 N1 105.7(3) . . ?
C6 C5 C4 116.2(3) . . ?
C6 C5 H5 121.9 . . ?
C4 C5 H5 121.9 . . ?
C5 C6 C7 121.5(4) . . ?
C5 C6 H6 119.2 . . ?
C7 C6 H6 119.2 . . ?
C8 C7 C6 122.4(3) . . ?
C8 C7 H7 118.8 . . ?
C6 C7 H7 118.8 . . ?
C7 C8 C9 116.3(3) . . ?
C7 C8 H8 121.8 . . ?
C9 C8 H8 121.8 . . ?
C4 C9 C8 121.0(3) . . ?
C4 C9 N2 106.9(3) . . ?
C8 C9 N2 132.1(3) . . ?
N2 C10 C11 112.5(3) . . ?
N2 C10 H10A 109.1 . . ?
C11 C10 H10A 109.1 . . ?
N2 C10 H10B 109.1 . . ?
C11 C10 H10B 109.1 . . ?
H10A C10 H10B 107.8 . . ?
C10 C11 C11 112.4(3) . 2_685 ?
C10 C11 H11A 109.1 . . ?
C11 C11 H11A 109.1 2_685 . ?
C10 C11 H11B 109.1 . . ?
C11 C11 H11B 109.1 2_685 . ?
H11A C11 H11B 107.8 . . ?
C3 N1 C4 109.8(2) . . ?
C3 N1 H1 125.1 . . ?
C4 N1 H1 125.1 . . ?
C3 N2 C9 108.3(3) . . ?
C3 N2 C10 124.9(3) . . ?
C9 N2 C10 126.8(3) . . ?
Mo3 O1 Mo1 116.07(11) . . ?
Mo1 O3 Mo3 116.42(9) . 2_766 ?
Mo1 O4 Mo2 116.62(10) . . ?
Mo3 O5 Mo3 180.0 . 2_766 ?
Mo3 O5 Mo1 89.816(13) . 2_766 ?
Mo3 O5 Mo1 90.184(13) 2_766 2_766 ?
Mo3 O5 Mo1 90.184(13) . . ?
Mo3 O5 Mo1 89.816(12) 2_766 . ?
Mo1 O5 Mo1 180.0 2_766 . ?
Mo3 O5 Mo2 89.499(14) . . ?
Mo3 O5 Mo2 90.501(14) 2_766 . ?
Mo1 O5 Mo2 90.083(14) 2_766 . ?
Mo1 O5 Mo2 89.917(14) . . ?
Mo3 O5 Mo2 90.501(14) . 2_766 ?
Mo3 O5 Mo2 89.499(14) 2_766 2_766 ?
Mo1 O5 Mo2 89.917(14) 2_766 2_766 ?
Mo1 O5 Mo2 90.083(14) . 2_766 ?
Mo2 O5 Mo2 180.000(8) . 2_766 ?
Mo2 O6 Mo3 115.67(10) . 2_766 ?
Mo2 O8 Mo1 117.24(11) . 2_766 ?
Mo3 O9 Mo2 116.81(10) . . ?
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_distance
_geom_bond_site_symmetry_2
_geom_bond_publ_flag
Mo1 O2 1.677(2) . ?
Mo1 O3 1.886(2) . ?
Mo1 O4 1.919(2) . ?
Mo1 O8 1.921(2) 2_766 ?
Mo1 O1 1.962(2) . ?
Mo1 O5 2.3155(3) . ?
Mo2 O7 1.668(2) . ?
Mo2 O8 1.918(2) . ?
Mo2 O6 1.928(2) . ?
Mo2 O4 1.928(2) . ?
Mo2 O9 1.939(2) . ?
Mo2 O5 2.3174(4) . ?
Mo3 O10 1.678(2) . ?
Mo3 O9 1.888(2) . ?
Mo3 O1 1.901(2) . ?
Mo3 O6 1.957(2) 2_766 ?
Mo3 O3 1.957(2) 2_766 ?
Mo3 O5 2.3123(3) . ?
C1 C2 1.497(5) . ?
C1 H1A 0.9600 . ?
C1 H1B 0.9600 . ?
C1 H1C 0.9600 . ?
C2 C3 1.475(5) . ?
C2 H2A 0.9700 . ?
C2 H2B 0.9700 . ?
C3 N1 1.321(4) . ?
C3 N2 1.345(4) . ?
C4 C5 1.382(5) . ?
C4 C9 1.392(4) . ?
C4 N1 1.392(4) . ?
C5 C6 1.375(5) . ?
C5 H5 0.9300 . ?
C6 C7 1.398(5) . ?
C6 H6 0.9300 . ?
C7 C8 1.371(5) . ?
C7 H7 0.9300 . ?
C8 C9 1.392(4) . ?
C8 H8 0.9300 . ?
C9 N2 1.393(4) . ?
C10 N2 1.471(4) . ?
C10 C11 1.505(4) . ?
C10 H10A 0.9700 . ?
C10 H10B 0.9700 . ?
C11 C11 1.520(6) 2_685 ?
C11 H11A 0.9700 . ?
C11 H11B 0.9700 . ?
N1 H1 0.8600 . ?
O3 Mo3 1.957(2) 2_766 ?
O5 Mo3 2.3123(3) 2_766 ?
O5 Mo1 2.3155(3) 2_766 ?
O5 Mo2 2.3174(4) 2_766 ?
O6 Mo3 1.957(2) 2_766 ?
O8 Mo1 1.921(2) 2_766 ?
loop_
_geom_torsion_atom_site_label_1
_geom_torsion_atom_site_label_2
_geom_torsion_atom_site_label_3
_geom_torsion_atom_site_label_4
_geom_torsion
_geom_torsion_site_symmetry_1
_geom_torsion_site_symmetry_2
_geom_torsion_site_symmetry_3
_geom_torsion_site_symmetry_4
_geom_torsion_publ_flag
C1 C2 C3 N1 -15.0(6) . . . . ?
C1 C2 C3 N2 167.7(3) . . . . ?
C9 C4 C5 C6 -0.8(5) . . . . ?
N1 C4 C5 C6 -179.2(3) . . . . ?
C4 C5 C6 C7 0.6(5) . . . . ?
C5 C6 C7 C8 0.0(6) . . . . ?
C6 C7 C8 C9 -0.4(5) . . . . ?
C5 C4 C9 C8 0.4(5) . . . . ?
N1 C4 C9 C8 179.1(3) . . . . ?
C5 C4 C9 N2 -178.7(3) . . . . ?
N1 C4 C9 N2 0.0(3) . . . . ?
C7 C8 C9 C4 0.2(5) . . . . ?
C7 C8 C9 N2 179.0(3) . . . . ?
N2 C10 C11 C11 168.8(3) . . . 2_685 ?
N2 C3 N1 C4 0.6(4) . . . . ?
C2 C3 N1 C4 -177.1(3) . . . . ?
C5 C4 N1 C3 178.2(3) . . . . ?
C9 C4 N1 C3 -0.4(3) . . . . ?
N1 C3 N2 C9 -0.5(4) . . . . ?
C2 C3 N2 C9 177.2(3) . . . . ?
N1 C3 N2 C10 179.5(3) . . . . ?
C2 C3 N2 C10 -2.7(5) . . . . ?
C4 C9 N2 C3 0.3(3) . . . . ?
C8 C9 N2 C3 -178.6(3) . . . . ?
C4 C9 N2 C10 -179.8(3) . . . . ?
C8 C9 N2 C10 1.3(5) . . . . ?
C11 C10 N2 C3 -82.6(4) . . . . ?
C11 C10 N2 C9 97.5(4) . . . . ?
O10 Mo3 O1 Mo1 -179.30(12) . . . . ?
O9 Mo3 O1 Mo1 76.13(12) . . . . ?
O6 Mo3 O1 Mo1 -78.04(12) 2_766 . . . ?
O3 Mo3 O1 Mo1 -5.9(3) 2_766 . . . ?
O5 Mo3 O1 Mo1 -1.18(9) . . . . ?
O2 Mo1 O1 Mo3 -178.66(13) . . . . ?
O3 Mo1 O1 Mo3 0.3(3) . . . . ?
O4 Mo1 O1 Mo3 -76.27(12) . . . . ?
O8 Mo1 O1 Mo3 78.16(12) 2_766 . . . ?
O5 Mo1 O1 Mo3 1.19(9) . . . . ?
O2 Mo1 O3 Mo3 -178.45(13) . . . 2_766 ?
O4 Mo1 O3 Mo3 78.66(11) . . . 2_766 ?
O8 Mo1 O3 Mo3 -74.58(11) 2_766 . . 2_766 ?
O1 Mo1 O3 Mo3 2.6(3) . . . 2_766 ?
O5 Mo1 O3 Mo3 1.71(8) . . . 2_766 ?
O2 Mo1 O4 Mo2 -178.61(13) . . . . ?
O3 Mo1 O4 Mo2 -75.44(12) . . . . ?
O8 Mo1 O4 Mo2 7.5(3) 2_766 . . . ?
O1 Mo1 O4 Mo2 79.05(12) . . . . ?
O5 Mo1 O4 Mo2 2.18(9) . . . . ?
O7 Mo2 O4 Mo1 177.88(13) . . . . ?
O8 Mo2 O4 Mo1 -3.8(3) . . . . ?
O6 Mo2 O4 Mo1 75.27(12) . . . . ?
O9 Mo2 O4 Mo1 -78.97(12) . . . . ?
O5 Mo2 O4 Mo1 -2.18(9) . . . . ?
O10 Mo3 O5 Mo3 24(100) . . . 2_766 ?
O9 Mo3 O5 Mo3 157(100) . . . 2_766 ?
O1 Mo3 O5 Mo3 -111(100) . . . 2_766 ?
O6 Mo3 O5 Mo3 -20(100) 2_766 . . 2_766 ?
O3 Mo3 O5 Mo3 67(100) 2_766 . . 2_766 ?
O10 Mo3 O5 Mo1 -44(2) . . . 2_766 ?
O9 Mo3 O5 Mo1 89.25(7) . . . 2_766 ?
O1 Mo3 O5 Mo1 -179.10(7) . . . 2_766 ?
O6 Mo3 O5 Mo1 -88.47(6) 2_766 . . 2_766 ?
O3 Mo3 O5 Mo1 -1.26(6) 2_766 . . 2_766 ?
O10 Mo3 O5 Mo1 136(2) . . . . ?
O9 Mo3 O5 Mo1 -90.75(7) . . . . ?
O1 Mo3 O5 Mo1 0.90(7) . . . . ?
O6 Mo3 O5 Mo1 91.53(6) 2_766 . . . ?
O3 Mo3 O5 Mo1 178.74(6) 2_766 . . . ?
O10 Mo3 O5 Mo2 -134(2) . . . . ?
O9 Mo3 O5 Mo2 -0.84(7) . . . . ?
O1 Mo3 O5 Mo2 90.81(7) . . . . ?
O6 Mo3 O5 Mo2 -178.55(6) 2_766 . . . ?
O3 Mo3 O5 Mo2 -91.34(6) 2_766 . . . ?
O10 Mo3 O5 Mo2 46(2) . . . 2_766 ?
O9 Mo3 O5 Mo2 179.16(7) . . . 2_766 ?
O1 Mo3 O5 Mo2 -89.19(7) . . . 2_766 ?
O6 Mo3 O5 Mo2 1.45(6) 2_766 . . 2_766 ?
O3 Mo3 O5 Mo2 88.66(6) 2_766 . . 2_766 ?
O2 Mo1 O5 Mo3 10(7) . . . . ?
O3 Mo1 O5 Mo3 178.70(6) . . . . ?
O4 Mo1 O5 Mo3 87.88(7) . . . . ?
O8 Mo1 O5 Mo3 -89.65(7) 2_766 . . . ?
O1 Mo1 O5 Mo3 -0.88(7) . . . . ?
O2 Mo1 O5 Mo3 -170(7) . . . 2_766 ?
O3 Mo1 O5 Mo3 -1.30(6) . . . 2_766 ?
O4 Mo1 O5 Mo3 -92.12(7) . . . 2_766 ?
O8 Mo1 O5 Mo3 90.35(7) 2_766 . . 2_766 ?
O1 Mo1 O5 Mo3 179.12(7) . . . 2_766 ?
O2 Mo1 O5 Mo1 -172(100) . . . 2_766 ?
O3 Mo1 O5 Mo1 -4(100) . . . 2_766 ?
O4 Mo1 O5 Mo1 -94(100) . . . 2_766 ?
O8 Mo1 O5 Mo1 88(100) 2_766 . . 2_766 ?
O1 Mo1 O5 Mo1 177(100) . . . 2_766 ?
O2 Mo1 O5 Mo2 -79(7) . . . . ?
O3 Mo1 O5 Mo2 89.20(6) . . . . ?
O4 Mo1 O5 Mo2 -1.62(7) . . . . ?
O8 Mo1 O5 Mo2 -179.15(7) 2_766 . . . ?
O1 Mo1 O5 Mo2 -90.37(7) . . . . ?
O2 Mo1 O5 Mo2 101(7) . . . 2_766 ?
O3 Mo1 O5 Mo2 -90.80(6) . . . 2_766 ?
O4 Mo1 O5 Mo2 178.38(7) . . . 2_766 ?
O8 Mo1 O5 Mo2 0.85(7) 2_766 . . 2_766 ?
O1 Mo1 O5 Mo2 89.63(7) . . . 2_766 ?
O7 Mo2 O5 Mo3 -86(3) . . . . ?
O8 Mo2 O5 Mo3 90.67(7) . . . . ?
O6 Mo2 O5 Mo3 -178.53(6) . . . . ?
O4 Mo2 O5 Mo3 -88.57(7) . . . . ?
O9 Mo2 O5 Mo3 0.82(6) . . . . ?
O7 Mo2 O5 Mo3 94(3) . . . 2_766 ?
O8 Mo2 O5 Mo3 -89.33(7) . . . 2_766 ?
O6 Mo2 O5 Mo3 1.47(6) . . . 2_766 ?
O4 Mo2 O5 Mo3 91.43(7) . . . 2_766 ?
O9 Mo2 O5 Mo3 -179.18(6) . . . 2_766 ?
O7 Mo2 O5 Mo1 -176(47) . . . 2_766 ?
O8 Mo2 O5 Mo1 0.85(7) . . . 2_766 ?
O6 Mo2 O5 Mo1 91.65(6) . . . 2_766 ?
O4 Mo2 O5 Mo1 -178.39(7) . . . 2_766 ?
O9 Mo2 O5 Mo1 -88.99(7) . . . 2_766 ?
O7 Mo2 O5 Mo1 4(3) . . . . ?
O8 Mo2 O5 Mo1 -179.15(7) . . . . ?
O6 Mo2 O5 Mo1 -88.35(6) . . . . ?
O4 Mo2 O5 Mo1 1.61(7) . . . . ?
O9 Mo2 O5 Mo1 91.01(7) . . . . ?
O7 Mo2 O5 Mo2 -170(100) . . . 2_766 ?
O8 Mo2 O5 Mo2 7(100) . . . 2_766 ?
O6 Mo2 O5 Mo2 98(100) . . . 2_766 ?
O4 Mo2 O5 Mo2 -172(100) . . . 2_766 ?
O9 Mo2 O5 Mo2 -83(100) . . . 2_766 ?
O7 Mo2 O6 Mo3 179.64(13) . . . 2_766 ?
O8 Mo2 O6 Mo3 74.57(12) . . . 2_766 ?
O4 Mo2 O6 Mo3 -78.85(12) . . . 2_766 ?
O9 Mo2 O6 Mo3 -3.3(3) . . . 2_766 ?
O5 Mo2 O6 Mo3 -1.93(8) . . . 2_766 ?
O7 Mo2 O8 Mo1 178.76(13) . . . 2_766 ?
O6 Mo2 O8 Mo1 -78.43(12) . . . 2_766 ?
O4 Mo2 O8 Mo1 0.5(3) . . . 2_766 ?
O9 Mo2 O8 Mo1 75.56(12) . . . 2_766 ?
O5 Mo2 O8 Mo1 -1.16(9) . . . 2_766 ?
O10 Mo3 O9 Mo2 179.17(12) . . . . ?
O1 Mo3 O9 Mo2 -76.29(12) . . . . ?
O6 Mo3 O9 Mo2 6.2(3) 2_766 . . . ?
O3 Mo3 O9 Mo2 77.59(12) 2_766 . . . ?
O5 Mo3 O9 Mo2 1.12(9) . . . . ?
O7 Mo2 O9 Mo3 177.30(13) . . . . ?
O8 Mo2 O9 Mo3 -77.87(12) . . . . ?
O6 Mo2 O9 Mo3 0.3(3) . . . . ?
O4 Mo2 O9 Mo3 75.96(12) . . . . ?
O5 Mo2 O9 Mo3 -1.13(9) . . . . ?